PHOSPHOR BRONZE
· 기호 : 1종(C5102),2종(C5191),3종(C5210)
· 특성 : Cu에 Sn을 4.5%~9% 함유된 금속으로 강인성과 전연성이 풍부하여 SPRING성, 탄성을 요하는 곳에 사용됨. 우수한 탄성, 내마모성, 耐화학성
· 규격 : 0.2mm(t)~2.0mm(t), 1.5mm(w)~250w
Classification |
PHOSPHOR BRONZE |
|||
C5102 |
C5191 |
C5210 |
||
Chemical Composition(%) |
Cu Balance Sn:4.5-5.5 P:0.03-0.35 |
Cu balance Sn:5.5-7.0 P:0.03-0.35 |
Cu Balance Sn:7.0-9.0 P:0.03-0.35 Pb≤0.05, Fe≤0.1 |
|
Specific Gravity(gm/cm³) |
8.9 |
8.8 |
8.8 |
|
Expansion Conductivity(10-6/°C) |
17.8 |
18 |
18.2 |
|
Thermal Conductivity(W/(m·k)) |
71 |
67 |
63 |
|
Electrical Conductivity(%IACS, 20°C) |
15 |
13 |
11 |
|
Tensile Strength (kgf/mm²) |
O |
31MIN |
- |
- |
1/4H |
38-48 |
42-48 |
- |
|
1/2H |
48-58 |
52-58 |
52-58 |
|
3/4H |
- |
- |
- |
|
H |
58-68 |
62-68 |
62-68 |
|
EH |
63MIN |
66-72 |
71-77 |
|
SH |
- |
74MIN |
78MIN |
|
Elongation(%) |
O |
40MIN |
- |
- |
1/4H |
28MIN |
40MIN |
- |
|
1/2H |
15MIN |
30MIN |
30MIN |
|
3/4H |
- |
- |
25MIN |
|
H |
7MIN |
25MIN |
- |
|
EH |
4MIN |
10MIN |
15MIN |
|
SH | - | 2MIN | 11MIN | |
Vicker Hardness | O | - | - | - |
1/4H | 90-1230 | 120-140 | - | |
1/2H | 130-170 | 160-175 | 165-185 | |
3/4H | - | - | - | |
H | 170-190 | 180-200 | 190-210 | |
EH | 190MIN | 200-230 | 220-230 | |
SH | - | 220MIN | 230MIN |
COPPER
· 기호 : C1020,C1020
· 특성 : 우수한 전기전도성 및 열전도성, 높은 성형성, 耐 수소취성, 좋은 용접성, 납땜성, 우수한 가공성
· 규격 : 0.03mm(t)~2.0mm(t), 1.5mm(w)~250w
Classification |
HIGH CONCUTIVITY & ELECTRIC COPPER |
||||
C1020 |
C1100 |
C1201 |
C1220 |
||
Chemical composition(%) |
Cu:99.96min O₂:≤0.01 |
Cu:99.90min O₂:0.02-0.045 |
Cu:99.90min O₂:0.004-0.015 |
Cu:99.90min O₂:0.015-0.04 |
|
Specific Gravity(gm/cm³) |
8.94 |
8.94 |
8.94 |
8.94 |
|
Expansion Conductivity(10-6/°C) |
17.7 |
17.7 |
17.7 |
17.7 |
|
Thermal Conductivity(W/(m·k)) |
391 |
391 |
364 |
339 |
|
Electrical Conductivity(%IACS, 20°C) |
101 |
100 |
90 |
85 |
|
Tensile Strength(kgf/mm²) |
O |
23-26 |
23-26 |
23-26 |
23-26 |
1/4H |
26-28 |
26-28 |
26-28 |
26-28 |
|
1/2H |
29-32 |
29-32 |
29-32 |
29-32 |
|
3/4H |
- |
- |
- |
- |
|
H |
32MIN |
32MIN |
32MIN |
32MIN |
|
Elongation(%) |
O |
40MIN |
40MIN |
40MIN |
40MIN |
1/4H |
32MIN |
32MIN |
32MIN |
32MIN |
|
1/2H |
20-30 |
20-30 |
20-30 |
20-30 |
|
3/4H |
- |
- |
- |
- |
|
H |
- |
- |
- |
- |
|
Vicker Hardness |
O |
70MAX |
70MAX |
70MAX |
70MAX |
1/4H |
70-85 |
70-85 |
70-85 |
70-85 |
|
1/2H |
85-105 |
85-105 |
85-105 |
85-105 |
|
3/4H | - | - | - | - | |
H | 105MIN | 105MIN | 105MIN | 105MIN |
BRASS
· 기호 : 1종(C2600),2종A(C2680),2종B(C2720)
· 특성 : Cu에 Zn을 30~40%함유된 금속 , 우수한 드로잉성, 전연성, 높은강도와 내식성
· 규격 : 0.2mm(t)~2.0mm(t), 1.5mm(w)~250w
Classification |
BRASS |
|||
C2600 |
C2680 |
C2720 |
||
Chemical Composition(%) |
Cu:69.5-71.5 Zn Balance Pb:≤0.07 Fe:≤0.05 |
Cu:64.0-68.0 Zn Balance Pb:≤0.07 Fe:≤0.05 |
Cu:62.0-64.0 Zn Balance Pb:≤0.07 Fe:≤0.05 |
|
Specific Gravity(gm/cm³) |
8.55 |
8.47 |
8.47 |
|
Expansion Conductivity(10-6/°C) |
18 |
18 |
18 |
|
Thermal Conductivity(W/(m·k)) |
121 |
117 |
117 |
|
Electrical Conductivity(%IACS, 20°C) |
28 |
28 |
27 |
|
Tensile Strength (kgf/mm²) |
O |
37MAX |
37MAX |
37MAX |
1/4H |
37-39 |
37-39 |
37-39 |
|
1/2H |
39-44 |
39-44 |
39-44 |
|
3/4H |
- |
- |
- |
|
H |
45-50 |
45-50 |
45-50 |
|
EH |
51MIN |
51MIN |
51MIN |
|
Elongation(%) |
O |
52MIN |
52MIN |
52MIN |
1/4 |
49MIN |
49MIN |
49MIN |
|
1/2 |
28-38 |
28-38 |
28-38 |
|
3/4 |
- |
- |
- |
|
H |
16-24 |
16-24 |
16-24 |
|
EH |
5-15 |
5-15 |
5-15 |
|
Vicker Hardness |
O |
90MAX |
90MAX |
90MAX |
1/4 | 90-120 | 90-120 | 90-120 | |
1/2 | 125-140 | 125-140 | 125-140 | |
3/4 | - | - | - | |
H | 145-160 | 145-160 | 145-160 | |
EH | 165-180 | 165-180 | 165-180 |
베릴륨동 와이어
Alloy |
UNS No. |
SPEC. No. |
CHEMICAL COMPOSITION(%) |
|
25 |
C17200 |
ASTM B 196, 251, 643 |
Be |
1.8~2.0 |
QQ-C-530 |
Co + Ni |
0.2 MIN |
||
AMS 4650, 4651 |
Co + Ni + Fe |
0.6 MAX |
||
SAE J 461, 463 |
Cu + Be + Co + Ni + Fe |
99.5 MIN |
||
JIS H 3270 |
- |
- |
||
M25 |
C17300 |
ASTM B 196 |
Be |
1.8~2.0 |
QQ-C-530 |
Co + Ni |
0.2 MIN |
||
MIL-C-21657 |
Co + Ni + Fe |
0.6 MAX |
||
DIN 17672 |
Pb |
0.2~0.6 |
||
- |
Cu + Co + Ni + Fe + Pb |
99.5 MIN |
MECHANICAL SPECIFICATION |
|
TENSILE STRENGTH(MPA) |
655~896 |
ELONGATION(%) |
≥8 |
HARDNESS(Hv) |
185~275 |
WIRE |
DIA | 0.1~0.8mm |
PACKING | BOBBIN |
|
ROD |
DIA | 1.0~14.0mm |
LENGTH | 1.0~3.0m |
|
REMARK | TOLERANCE | 0/-0.005 |